Adhesion, Residual Stresses and Tribology of Rf Sputter Deposited Titanium Carbide Coatings
Pan, Alfred I-Tsung
This item is only available for download by members of the University of Illinois community. Students, faculty, and staff at the U of I may log in with your NetID and password to view the item. If you are trying to access an Illinois-restricted dissertation or thesis, you can request a copy through your library's Inter-Library Loan office or purchase a copy directly from ProQuest.
Permalink
https://hdl.handle.net/2142/67031
Description
Title
Adhesion, Residual Stresses and Tribology of Rf Sputter Deposited Titanium Carbide Coatings
Author(s)
Pan, Alfred I-Tsung
Issue Date
1981
Department of Study
Mechanical Engineering
Discipline
Mechanical Engineering
Degree Granting Institution
University of Illinois at Urbana-Champaign
Degree Name
Ph.D.
Degree Level
Dissertation
Keyword(s)
Engineering, Materials Science
Language
eng
Abstract
Mechanical properties of surface hard coatings depends strongly on both the adhesion of the coating to the substrate as well as the sign and magnitude of the residual stress in the coating. The residual stress in sputter deposited TiC films was found to be compressive and could be related to the trapped Ar concentration in the films. The Ar concentration, and hence the compressive stress, increased with decreasing Ar sputtering pressure, P(,Ar), due to the relationship between the substrate induced potential, V(,i), and P(,Ar). High compressive stress in the TiC films enable this brittle material to withstand high tensile strain. However, too high a compressive stress would induce a high Poisson tensile stress which result in the fracture of the interface and the bulging up of the film. Incorporation of moderate amount of oxygen in the TiC films during deposition will not cause compressive stress. However, high oxygen content in the film with O/Ti higher than 0.5 would lead to second phase segregation in the TiC(,x)O(,1-x) matrix and result in a high compressive stress.
Extremely good adhesion of sputter deposited TiC films to the 4140 steel substrates with an adhesive strength on the order of the shear strength of the steel was accomplished in this study. Improvement in the adhesion was achieved by reducing the oxygen content in the interface which produced a compositionally graded junction from TiC(,x)O(,1-x) in the interface to TiC in the bulk, both being the same structure.
Friction and wear properties of plastically loaded steel sliders against flat TiC coatings were found to be a function of apparent contact area. Reduction in the friction coefficient and in slider wear was achieved by the use of a photolithographically produced checkerboard structure with regularly spaced micro-reservoirs in the TiC films to reduce apparent contact area. The reduction in slider wear was also due to the trapping of wear debris inside the pockets of the checkerboard structure which decreased the abrasive slider wear caused by three-body-wear due to hard wear particles. Stick-slip motion of the slider was also reduced due to the intermitant breakage of asperity contact brought about by the regularly spaced micro-reservoirs structure.
Use this login method if you
don't
have an
@illinois.edu
email address.
(Oops, I do have one)
IDEALS migrated to a new platform on June 23, 2022. If you created
your account prior to this date, you will have to reset your password
using the forgot-password link below.