Excitons in cuprous oxide: high mobilities and strain confinement

Trauernicht, David Paul

This item is only available for download by members of the University of Illinois community. Students, faculty, and staff at the U of I may log in with your NetID and password to view the item. If you are trying to access an Illinois-restricted dissertation or thesis, you can request a copy through your library's Inter-Library Loan office or purchase a copy directly from ProQuest.

Permalink

https://hdl.handle.net/2142/25272

Description

Title
Excitons in cuprous oxide: high mobilities and strain confinement
Author(s)
Trauernicht, David Paul
Issue Date
1985
Doctoral Committee Chair(s)
Wolfe, J.P.
Department of Study
Physics
Discipline
Physics
Degree Name
Ph.D.
Degree Level
Dissertation
Keyword(s)
  • excitons
  • cuprous oxide
  • paraexciton
  • time-resolved luminescence imaging
  • parabolic potential
  • interparticle kinetics
Language
en
Abstract
"This thesis presents two studies of the spectral and spatial properties of excitons in the semiconductor cuprous oxide (CU0) at 2liquid helium temperatures. The lowest lying member of the yellow exciton series, the paraexciton, is the main focus of these studies. The technique cf time-resolved luminescence imaging was used to measure the transport properties of the paraexcitons. In addition, these excitons were bpatially confined in a strain-induced parabolic potential well where their thermodynamic properties and interparticle kinetics could be studied. Chapter 3 describes the technique used to measure the diffusion constant, D, and the drift mobility, 11, of paraexdtons, as well as a theoretical model to explain the unusual results. .An externally applied inhomO'::feIl-""'Ous stress gradient was used to provide the motive force for the mobility measurement. Very large values of D (~ 1000 2 7 2 cm Is) and 11 (-10cm /eV-s) were measured at a bath temperature of 1.2 K. Both these parameters exhibited anomalous temperature dep.:=.'ldences as well as a drastic dependence on the externally applied stress. A calculation of low temperature deformation-potential scattering of excitons with acoustic phonons, iv making none of the usual approximations which are valid at higher temperatures, resulted in good agreement between experiment and theory. The stress dependence is explained by an increased coupling to transverse acoustic phonons with increased applied stress. Chapter 4 explains the strain confinement technique, along with a derivation of the expected luminescence lineshapes and spatial profiles of excitons confined in the resulting parabolic potential well. Experimental results for paraexcitons using low power laser excitation are given and compared to theory. The discouraging result that the paraexcitons do not seem to thermalize in the well within their lifetime is obtained. Interparticle kinetics of the excitons i~ examined under increasing laser excitation yielding a significant sublinear dependence of the paraexciton density on absorbed laser power. Time-resolved measurements showed a very slow thermalization taking place, with lattice heating occurring at high laser intensities."
Type of Resource
text
Permalink
http://hdl.handle.net/2142/25272
Copyright and License Information
1985 David Paul Trauernicht

Owning Collections

Dissertations and Theses - Physics
Dissertations in Physics
Graduate Dissertations and Theses at Illinois PRIMARY
Graduate Theses and Dissertations at Illinois