University of Illinois Urbana-Champaign

Ultrahigh vacuum studies of the boundary lubrication of metals

McFadden, Christopher Frederick

This item is only available for download by members of the University of Illinois community. Students, faculty, and staff at the U of I may log in with your NetID and password to view the item. If you are trying to access an Illinois-restricted dissertation or thesis, you can request a copy through your library's Inter-Library Loan office or purchase a copy directly from ProQuest.

Permalink

https://hdl.handle.net/2142/22204

Description

Title
Ultrahigh vacuum studies of the boundary lubrication of metals
Author(s)
McFadden, Christopher Frederick
Issue Date
1996
Doctoral Committee Chair(s)
Gellman, A.J.
Department of Study
Chemistry
Discipline
Chemistry
Degree Granting Institution
University of Illinois at Urbana-Champaign
Degree Name
Ph.D.
Degree Level
Dissertation
Keyword(s)
  • Chemistry, Physical
  • Engineering, Mechanical
  • Engineering, Materials Science
Language
eng
Abstract
  • A novel ultrahigh vacuum (UHV) tribometer was used to study the tribological behavior of two Cu(111) surfaces modified by the adsorption of various atomic (sulfur, chlorine, iodine) and molecular (ethanol, trifluoroethanol, butanol, and heptafluorobutanol) species as a function of coverage. The friction behavior of clean Cu(111) surfaces was characterized by stick-slip sliding behavior and high static friction coefficients.
  • "Of the atomic species studied, only contaminant films formed by exposure to the atmosphere were effective as lubricants, in the sense that the sliding behavior changed from ""stick-slip"" to ""slip"" and the friction coefficient was significantly lower than that of the clean surfaces. As the contaminant film thickness was reduced by sputtering, a transition to higher friction coefficients and stick-slip behavior occurred at film thicknesses $\sim$5-8 A. The problem of the poorly defined thickness and composition of the contaminant films was addressed by making friction measurements on surfaces that were cleaned and then modified by the adsorption of sulfur, chlorine and iodine. Compared to the clean surfaces, the friction coefficient was reduced only slightly (sulfur, chlorine) or not at all (iodine), even at saturation. From these results, it can be concluded that the minimum thickness is greater than $\sim$2 A, the effective ionic radius of sulfur, chlorine or iodine atoms. The difference in the lubricating ability of the three species was small and of uncertain significance."
  • "For the alcohols, friction measurements were made at coverages ranging from submonolayer to several multilayers. These alcohols showed similar friction behavior as a function of coverage. At coverages below one monolayer the surfaces were not well lubricated--the sliding behavior was stick-slip and the friction coefficients were high, as for the surfaces modified with sulfur, chlorine and iodine. At coverages greater than one monolayer the friction coefficient was significantly reduced and decreased monotonically with increasing coverage. The transition from ""stick-slip"" to ""slip"" sliding behavior was reached at coverages of 2-7 ML. The friction coefficient continued to decrease with increasing coverage, reaching a limiting value only at coverages of several multilayers."
Type of Resource
text
Permalink
http://hdl.handle.net/2142/22204
Copyright and License Information
Copyright 1996 McFadden, Christopher Frederick

Owning Collections

Graduate Dissertations and Theses at Illinois PRIMARY
Graduate Theses and Dissertations at Illinois
Dissertations and Theses - Chemistry