Quenching of porous silicon photoluminescence by deposition of metal adsorbates
Andsager, David Kent
This item is only available for download by members of the University of Illinois community. Students, faculty, and staff at the U of I may log in with your NetID and password to view the item. If you are trying to access an Illinois-restricted dissertation or thesis, you can request a copy through your library's Inter-Library Loan office or purchase a copy directly from ProQuest.
Permalink
https://hdl.handle.net/2142/20093
Description
Title
Quenching of porous silicon photoluminescence by deposition of metal adsorbates
Author(s)
Andsager, David Kent
Issue Date
1994
Doctoral Committee Chair(s)
Nayfeh, Munir H.
Department of Study
Physics
Discipline
Physics
Degree Granting Institution
University of Illinois at Urbana-Champaign
Degree Name
Ph.D.
Degree Level
Dissertation
Keyword(s)
Physics, Condensed Matter
Physics, Optics
Language
eng
Abstract
Luminescent porous silicon is formed by anodization of silicon in HF acid in the dark and then under UV illumination. When illuminated with UV, samples exhibit a bright orange photoluminescence with a quantum efficiency of order a few percent. Porous silicon is characterized as a very complex network of interconnecting pores which range in size from 1 nm to 100 nm. It has a surface area of order 500 m$\sp2$/cm$\sp3$. The mechanism responsible for efficient luminescence of porous silicon is unknown, although there is a growing consensus that quantum confinement is necessary element to any successful explanation. We have attempted to increase understanding in porous silicon by a series of experiments in which luminescence is quenched. We have performed experiments in which the luminescence was quenched by immersion in metal ion solutions. In these experiments, we found that those ions solutions which caused quenching required a metal cation with a positive standard reduction potential. In this case, the metal ion was electrochemically deposited onto the surface of the porous silicon. Numerous Auger electron spectroscopy measurements indicate that the metal is present in the porous silicon at significant concentrations ($\sim$5-15%) for those samples in which the porous silicon was removed from solution as soon as the photoluminescence had been quenched as observed by eye. SEM measurements show no significant topographic differences between luminescent and quenched porous silicon samples. We have performed experiments in which metals were evaporated onto the surface of porous silicon. We have found for experiments involving evaporation of metal onto the surface of luminescent porous silicon that only copper metal evaporated onto p-type porous silicon has caused quenching of photoluminescence. Copper was evaporated onto p- and n-type porous silicon, but only copper evaporated onto p-type porous silicon caused quenching of the photoluminescence. Significant diffusion was noted only for copper evaporated onto p-type porous silicon; thus, the presence of copper in porous silicon appears sufficient to quench photoluminescence in porous silicon.
Use this login method if you
don't
have an
@illinois.edu
email address.
(Oops, I do have one)
IDEALS migrated to a new platform on June 23, 2022. If you created
your account prior to this date, you will have to reset your password
using the forgot-password link below.